JINSOR Types of Kuralon(Vinylon) Filament

Property

Type

1239

1225-7

1203-2

5501

5506

5508-1

5516-1

Thickness

(dtex)

1330

1100

1330

2000

1330

1100

2000

Number of Filament

fila

200

200

200

1000

600

600

1000

Breaking Strength

N

110

78

90

196

128

105

238

Tenacity

cN/dtex
g/dr
GPa

8.2
9.3
1.06

7.1
8.0
0.93

6.8
7.7
0.88

9.8
11.1
1.27

9.6
10.9
1.25

9.5
10.8
1.23

11.9
13.5
1.55

Elongation at break

%

7.7

10.0

13.5

6.6

8.0

9.0

6.4

Young's Modulus

cN/dtex
GPa

177
23.0

159
20.7

137
17.8

203
26.4

177
23.0

168
21.8

260
33.8

Dry heat shrinkage(160C,30min)

%

0.8

0.8

0.8

0.6

0.6

0.4

0.4

Boiling shrinkage(100C,30min)

%

4.5

4.5

4.5

2.5

2.5

2.0

2.2

Specific gravity

g/cm3

1.3

Melting point

C

over 240

Commercial moisture regain

%

5

Type

Kuralon
1239

Kuralon
5501

Kuralon
5516-1

Rayon
SuperIII

Polyester
HMLS

Nylon
6

Kevlar
29

Thickness(dtex)

1330

2000

2000

1830

1110

930

1670

Number of Filament

200

1000

1000

1100

250

96

1000

Breaking Strength(N)

110

196

238

75

86

75

324

Tenacity(cN/dtex)

8.2

9.8

11.9

4.1

7.8

8.1

19.4

Elongation at break(%)

7.7

6.6

6.4

12.9

11.9

19.4

3.9

Young's Modulus(cN/dtex)

177

203

260

85

110

34

493

Dry heat shrinkage(%)

0.8

0.6

0.4

1.8

7.0

6.5

0.0

Specific gravity(g/cm3)

1.3

1.3

1.3

1.52

1.38

1.14

1.41

Commercial moisture regain(%)

5

5

5

11.0

0.4

4.5

7.0